EN 1.6958 Steel vs. EN 1.8826 Steel

Both EN 1.6958 steel and EN 1.8826 steel are iron alloys. They have a moderately high 95% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.6958 steel and the bottom bar is EN 1.8826 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 340
190
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 16
19
Fatigue Strength, MPa 700
330
Impact Strength: V-Notched Charpy, J 63
68
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 700
390
Tensile Strength: Ultimate (UTS), MPa 1140
630
Tensile Strength: Yield (Proof), MPa 1070
480

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 450
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 47
49
Thermal Expansion, µm/m-K 11
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.9
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 9.1
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 5.0
2.3
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 2.0
1.6
Embodied Energy, MJ/kg 27
21
Embodied Water, L/kg 60
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 180
110
Resilience: Unit (Modulus of Resilience), kJ/m3 3050
620
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 40
22
Strength to Weight: Bending, points 31
21
Thermal Diffusivity, mm2/s 13
13
Thermal Shock Resistance, points 39
18

Alloy Composition

Aluminum (Al), % 0.0050 to 0.050
0.020 to 0.040
Carbon (C), % 0.25 to 0.3
0 to 0.16
Chromium (Cr), % 1.2 to 1.7
0
Iron (Fe), % 92.6 to 94.5
96.5 to 99.98
Manganese (Mn), % 0.2 to 0.5
0 to 1.7
Molybdenum (Mo), % 0.35 to 0.55
0 to 0.2
Nickel (Ni), % 3.3 to 3.8
0 to 0.5
Niobium (Nb), % 0
0 to 0.050
Nitrogen (N), % 0
0 to 0.020
Phosphorus (P), % 0 to 0.020
0 to 0.025
Silicon (Si), % 0.15 to 0.3
0 to 0.6
Sulfur (S), % 0 to 0.015
0 to 0.010
Titanium (Ti), % 0
0 to 0.050
Vanadium (V), % 0 to 0.12
0 to 0.1