EN 1.7016 Steel vs. EN 1.8153 Steel

Both EN 1.7016 steel and EN 1.8153 steel are iron alloys. They have a very high 98% of their average alloy composition in common.

For each property being compared, the top bar is EN 1.7016 steel and the bottom bar is EN 1.8153 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 130 to 170
200 to 570
Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
72
Tensile Strength: Ultimate (UTS), MPa 450 to 1390
670 to 2040

Thermal Properties

Latent Heat of Fusion, J/g 250
270
Maximum Temperature: Mechanical, °C 420
410
Melting Completion (Liquidus), °C 1460
1440
Melting Onset (Solidus), °C 1420
1390
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 45
45
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
8.7

Otherwise Unclassified Properties

Base Metal Price, % relative 2.2
2.1
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 1.4
1.8
Embodied Energy, MJ/kg 19
25
Embodied Water, L/kg 50
48

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 16 to 49
24 to 74
Strength to Weight: Bending, points 17 to 35
22 to 46
Thermal Diffusivity, mm2/s 12
12
Thermal Shock Resistance, points 13 to 41
20 to 62

Alloy Composition

Carbon (C), % 0.14 to 0.2
0.56 to 0.64
Chromium (Cr), % 0.7 to 1.0
0.2 to 0.4
Copper (Cu), % 0 to 0.25
0
Iron (Fe), % 97.3 to 98.6
95.7 to 96.9
Manganese (Mn), % 0.6 to 0.9
0.7 to 1.0
Phosphorus (P), % 0 to 0.025
0 to 0.025
Silicon (Si), % 0 to 0.3
1.5 to 2.0
Sulfur (S), % 0 to 0.025
0 to 0.025
Vanadium (V), % 0
0.1 to 0.2