EN 1.7102 Steel vs. C84000 Brass
EN 1.7102 steel belongs to the iron alloys classification, while C84000 brass belongs to the copper alloys. There are 25 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is EN 1.7102 steel and the bottom bar is C84000 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 200 to 480 | |
| 65 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 110 |
| Poisson's Ratio | 0.29 | |
| 0.33 |
| Shear Modulus, GPa | 72 | |
| 42 |
| Tensile Strength: Ultimate (UTS), MPa | 670 to 2010 | |
| 250 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 190 |
| Maximum Temperature: Mechanical, °C | 410 | |
| 170 |
| Melting Completion (Liquidus), °C | 1440 | |
| 1040 |
| Melting Onset (Solidus), °C | 1400 | |
| 940 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 380 |
| Thermal Conductivity, W/m-K | 47 | |
| 72 |
| Thermal Expansion, µm/m-K | 13 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.4 | |
| 16 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.6 | |
| 17 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.2 | |
| 30 |
| Density, g/cm3 | 7.7 | |
| 8.6 |
| Embodied Carbon, kg CO2/kg material | 1.5 | |
| 3.0 |
| Embodied Energy, MJ/kg | 20 | |
| 49 |
| Embodied Water, L/kg | 48 | |
| 330 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 25 | |
| 19 |
| Strength to Weight: Axial, points | 24 to 72 | |
| 8.2 |
| Strength to Weight: Bending, points | 22 to 46 | |
| 10 |
| Thermal Diffusivity, mm2/s | 13 | |
| 22 |
| Thermal Shock Resistance, points | 20 to 60 | |
| 9.0 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Aluminum (Al), % | 0 | |
| 0 to 0.0050 |
| Antimony (Sb), % | 0 | |
| 0 to 0.020 |
| Boron (B), % | 0 | |
| 0 to 0.1 |
| Carbon (C), % | 0.51 to 0.59 | |
| 0 |
| Chromium (Cr), % | 0.5 to 0.8 | |
| 0 |
| Copper (Cu), % | 0 | |
| 82 to 89 |
| Iron (Fe), % | 96.2 to 97.3 | |
| 0 to 0.4 |
| Lead (Pb), % | 0 | |
| 0 to 0.090 |
| Manganese (Mn), % | 0.5 to 0.8 | |
| 0 to 0.010 |
| Nickel (Ni), % | 0 | |
| 0.5 to 2.0 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.050 |
| Silicon (Si), % | 1.2 to 1.6 | |
| 0 to 0.0050 |
| Sulfur (S), % | 0 to 0.025 | |
| 0.1 to 0.65 |
| Tin (Sn), % | 0 | |
| 2.0 to 4.0 |
| Zinc (Zn), % | 0 | |
| 5.0 to 14 |
| Zirconium (Zr), % | 0 | |
| 0 to 0.1 |
| Residuals, % | 0 | |
| 0 to 0.7 |