EN 1.7117 Steel vs. AWS E219

Both EN 1.7117 steel and AWS E219 are iron alloys. They have 66% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is EN 1.7117 steel and the bottom bar is AWS E219.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 72
78
Tensile Strength: Ultimate (UTS), MPa 660 to 1930
690

Thermal Properties

Latent Heat of Fusion, J/g 270
290
Melting Completion (Liquidus), °C 1440
1400
Melting Onset (Solidus), °C 1400
1360
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 43
14
Thermal Expansion, µm/m-K 13
15

Otherwise Unclassified Properties

Base Metal Price, % relative 2.6
15
Density, g/cm3 7.7
7.7
Embodied Carbon, kg CO2/kg material 1.5
3.1
Embodied Energy, MJ/kg 21
44
Embodied Water, L/kg 51
160

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 24 to 69
25
Strength to Weight: Bending, points 22 to 44
23
Thermal Diffusivity, mm2/s 12
3.8
Thermal Shock Resistance, points 20 to 58
17

Alloy Composition

Carbon (C), % 0.49 to 0.56
0 to 0.060
Chromium (Cr), % 0.7 to 1.0
19 to 21.5
Copper (Cu), % 0
0 to 0.75
Iron (Fe), % 95.2 to 96.4
58.6 to 67.4
Manganese (Mn), % 0.7 to 1.0
8.0 to 10
Molybdenum (Mo), % 0
0 to 0.75
Nickel (Ni), % 0.5 to 0.7
5.5 to 7.0
Nitrogen (N), % 0
0.1 to 0.3
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 1.2 to 1.5
0 to 1.0
Sulfur (S), % 0 to 0.025
0 to 0.030