EN 1.7149 Steel vs. ASTM Grade HP Steel

Both EN 1.7149 steel and ASTM grade HP steel are iron alloys. They have a modest 38% of their average alloy composition in common, which, by itself, doesn't mean much. There are 23 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is EN 1.7149 steel and the bottom bar is ASTM grade HP steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150 to 180
140
Elastic (Young's, Tensile) Modulus, GPa 190
200
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
78
Tensile Strength: Ultimate (UTS), MPa 500 to 1460
490

Thermal Properties

Latent Heat of Fusion, J/g 250
320
Maximum Temperature: Mechanical, °C 420
1100
Melting Completion (Liquidus), °C 1460
1370
Melting Onset (Solidus), °C 1420
1330
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 46
12
Thermal Expansion, µm/m-K 13
16

Otherwise Unclassified Properties

Base Metal Price, % relative 2.3
34
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.5
5.8
Embodied Energy, MJ/kg 19
82
Embodied Water, L/kg 52
220

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 18 to 52
17
Strength to Weight: Bending, points 18 to 36
17
Thermal Diffusivity, mm2/s 12
3.2
Thermal Shock Resistance, points 15 to 42
11

Alloy Composition

Carbon (C), % 0.17 to 0.22
0.35 to 0.75
Chromium (Cr), % 1.0 to 1.3
24 to 28
Copper (Cu), % 0 to 0.25
0
Iron (Fe), % 96.5 to 97.7
29.2 to 42.7
Manganese (Mn), % 1.1 to 1.4
0 to 2.0
Molybdenum (Mo), % 0
0 to 0.5
Nickel (Ni), % 0
33 to 37
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 0 to 0.3
0 to 2.5
Sulfur (S), % 0.020 to 0.040
0 to 0.040