EN 1.7216 Steel vs. EN 1.1151 Steel

Both EN 1.7216 steel and EN 1.1151 steel are iron alloys. They have a very high 99% of their average alloy composition in common.

For each property being compared, the top bar is EN 1.7216 steel and the bottom bar is EN 1.1151 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200 to 280
130 to 150
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 12 to 23
21 to 26
Fatigue Strength, MPa 290 to 440
180 to 240
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 410 to 560
300 to 330
Tensile Strength: Ultimate (UTS), MPa 650 to 930
460 to 520
Tensile Strength: Yield (Proof), MPa 400 to 690
240 to 340

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 420
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 46
50
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 2.4
2.1
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.5
1.4
Embodied Energy, MJ/kg 20
19
Embodied Water, L/kg 50
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110 to 130
98 to 100
Resilience: Unit (Modulus of Resilience), kJ/m3 430 to 1280
160 to 310
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 23 to 33
16 to 18
Strength to Weight: Bending, points 21 to 27
17 to 18
Thermal Diffusivity, mm2/s 12
13
Thermal Shock Resistance, points 19 to 27
15 to 16

Alloy Composition

Carbon (C), % 0.27 to 0.34
0.17 to 0.24
Chromium (Cr), % 0.8 to 1.2
0 to 0.4
Iron (Fe), % 97.2 to 98.4
97.7 to 99.43
Manganese (Mn), % 0.35 to 0.6
0.4 to 0.7
Molybdenum (Mo), % 0.15 to 0.3
0 to 0.1
Nickel (Ni), % 0
0 to 0.4
Phosphorus (P), % 0 to 0.035
0 to 0.035
Silicon (Si), % 0 to 0.35
0 to 0.4
Sulfur (S), % 0 to 0.035
0 to 0.035

Comparable Variants