EN 1.7220 Steel vs. Z13004 Zinc

EN 1.7220 steel belongs to the iron alloys classification, while Z13004 zinc belongs to the zinc alloys. There are 24 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is EN 1.7220 steel and the bottom bar is Z13004 zinc.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
87
Poisson's Ratio 0.29
0.25
Shear Modulus, GPa 73
35
Tensile Strength: Ultimate (UTS), MPa 520 to 1720
93

Thermal Properties

Latent Heat of Fusion, J/g 250
110
Maximum Temperature: Mechanical, °C 420
90
Melting Completion (Liquidus), °C 1460
410
Melting Onset (Solidus), °C 1420
390
Specific Heat Capacity, J/kg-K 470
390
Thermal Conductivity, W/m-K 44
110
Thermal Expansion, µm/m-K 13
26

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
27
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
37

Otherwise Unclassified Properties

Base Metal Price, % relative 2.5
11
Density, g/cm3 7.8
6.6
Embodied Carbon, kg CO2/kg material 1.5
2.8
Embodied Energy, MJ/kg 20
53
Embodied Water, L/kg 51
340

Common Calculations

Stiffness to Weight: Axial, points 13
7.4
Stiffness to Weight: Bending, points 24
23
Strength to Weight: Axial, points 18 to 61
3.9
Strength to Weight: Bending, points 18 to 41
7.0
Thermal Diffusivity, mm2/s 12
44
Thermal Shock Resistance, points 15 to 50
2.9

Alloy Composition

Aluminum (Al), % 0
0 to 0.0020
Cadmium (Cd), % 0
0 to 0.0030
Carbon (C), % 0.3 to 0.37
0
Chromium (Cr), % 0.9 to 1.2
0
Copper (Cu), % 0
0 to 0.0030
Iron (Fe), % 96.8 to 98.1
0 to 0.0030
Lead (Pb), % 0
0 to 0.0030
Manganese (Mn), % 0.6 to 0.9
0
Molybdenum (Mo), % 0.15 to 0.3
0
Phosphorus (P), % 0 to 0.035
0
Silicon (Si), % 0 to 0.4
0
Sulfur (S), % 0 to 0.035
0
Tin (Sn), % 0
0 to 0.0010
Zinc (Zn), % 0
99.985 to 100