EN 1.7227 Steel vs. EN 1.4449 Stainless Steel

Both EN 1.7227 steel and EN 1.4449 stainless steel are iron alloys. They have 68% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is EN 1.7227 steel and the bottom bar is EN 1.4449 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
78
Tensile Strength: Ultimate (UTS), MPa 540 to 1850
620

Thermal Properties

Latent Heat of Fusion, J/g 250
290
Maximum Temperature: Mechanical, °C 420
960
Melting Completion (Liquidus), °C 1460
1440
Melting Onset (Solidus), °C 1420
1400
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 46
15
Thermal Expansion, µm/m-K 13
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 2.5
19
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.5
3.9
Embodied Energy, MJ/kg 20
54
Embodied Water, L/kg 51
150

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 19 to 65
22
Strength to Weight: Bending, points 19 to 43
20
Thermal Diffusivity, mm2/s 12
4.0
Thermal Shock Resistance, points 16 to 54
14

Alloy Composition

Carbon (C), % 0.38 to 0.45
0 to 0.035
Chromium (Cr), % 0.9 to 1.2
17 to 18.2
Copper (Cu), % 0 to 0.25
0 to 1.0
Iron (Fe), % 96.5 to 98
62.4 to 69.3
Manganese (Mn), % 0.6 to 0.9
0 to 2.0
Molybdenum (Mo), % 0.15 to 0.3
2.3 to 2.8
Nickel (Ni), % 0
11.5 to 12.5
Nitrogen (N), % 0
0 to 0.080
Phosphorus (P), % 0 to 0.025
0 to 0.045
Silicon (Si), % 0 to 0.3
0 to 1.0
Sulfur (S), % 0.020 to 0.040
0 to 0.015