EN 1.7227 Steel vs. EN 1.7335 Steel

Both EN 1.7227 steel and EN 1.7335 steel are iron alloys. Their average alloy composition is basically identical. There are 24 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is EN 1.7227 steel and the bottom bar is EN 1.7335 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Tensile Strength: Ultimate (UTS), MPa 540 to 1850
500 to 520

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 420
430
Melting Completion (Liquidus), °C 1460
1470
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 46
44
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 2.5
2.8
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.5
1.6
Embodied Energy, MJ/kg 20
21
Embodied Water, L/kg 51
52

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 19 to 65
18
Strength to Weight: Bending, points 19 to 43
18
Thermal Diffusivity, mm2/s 12
12
Thermal Shock Resistance, points 16 to 54
15

Alloy Composition

Carbon (C), % 0.38 to 0.45
0.080 to 0.18
Chromium (Cr), % 0.9 to 1.2
0.7 to 1.2
Copper (Cu), % 0 to 0.25
0 to 0.3
Iron (Fe), % 96.5 to 98
96.4 to 98.4
Manganese (Mn), % 0.6 to 0.9
0.4 to 1.0
Molybdenum (Mo), % 0.15 to 0.3
0.4 to 0.6
Nitrogen (N), % 0
0 to 0.012
Phosphorus (P), % 0 to 0.025
0 to 0.025
Silicon (Si), % 0 to 0.3
0 to 0.35
Sulfur (S), % 0.020 to 0.040
0 to 0.010