EN 1.7233 Steel vs. 6105 Aluminum
EN 1.7233 steel belongs to the iron alloys classification, while 6105 aluminum belongs to the aluminum alloys. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is EN 1.7233 steel and the bottom bar is 6105 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 68 |
| Elongation at Break, % | 18 to 23 | |
| 9.0 to 16 |
| Fatigue Strength, MPa | 270 to 530 | |
| 95 to 130 |
| Poisson's Ratio | 0.29 | |
| 0.33 |
| Shear Modulus, GPa | 73 | |
| 26 |
| Shear Strength, MPa | 450 to 590 | |
| 120 to 170 |
| Tensile Strength: Ultimate (UTS), MPa | 700 to 960 | |
| 190 to 280 |
| Tensile Strength: Yield (Proof), MPa | 380 to 780 | |
| 120 to 270 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 410 |
| Maximum Temperature: Mechanical, °C | 430 | |
| 160 |
| Melting Completion (Liquidus), °C | 1460 | |
| 650 |
| Melting Onset (Solidus), °C | 1420 | |
| 600 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 900 |
| Thermal Conductivity, W/m-K | 39 | |
| 180 to 190 |
| Thermal Expansion, µm/m-K | 13 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.4 | |
| 46 to 50 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.5 | |
| 150 to 170 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 3.0 | |
| 9.5 |
| Density, g/cm3 | 7.8 | |
| 2.7 |
| Embodied Carbon, kg CO2/kg material | 1.6 | |
| 8.3 |
| Embodied Energy, MJ/kg | 21 | |
| 150 |
| Embodied Water, L/kg | 53 | |
| 1180 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 to 200 | |
| 25 to 27 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 380 to 1630 | |
| 100 to 550 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 51 |
| Strength to Weight: Axial, points | 25 to 34 | |
| 20 to 29 |
| Strength to Weight: Bending, points | 22 to 28 | |
| 28 to 35 |
| Thermal Diffusivity, mm2/s | 11 | |
| 72 to 79 |
| Thermal Shock Resistance, points | 21 to 28 | |
| 8.6 to 12 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Aluminum (Al), % | 0 | |
| 97.2 to 99 |
| Carbon (C), % | 0.39 to 0.45 | |
| 0 |
| Chromium (Cr), % | 1.2 to 1.5 | |
| 0 to 0.1 |
| Copper (Cu), % | 0 | |
| 0 to 0.1 |
| Iron (Fe), % | 96.2 to 97.5 | |
| 0 to 0.35 |
| Magnesium (Mg), % | 0 | |
| 0.45 to 0.8 |
| Manganese (Mn), % | 0.4 to 0.7 | |
| 0 to 0.1 |
| Molybdenum (Mo), % | 0.5 to 0.7 | |
| 0 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 |
| Silicon (Si), % | 0 to 0.4 | |
| 0.6 to 1.0 |
| Sulfur (S), % | 0 to 0.035 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 0 to 0.1 |
| Zinc (Zn), % | 0 | |
| 0 to 0.1 |
| Residuals, % | 0 | |
| 0 to 0.15 |