EN 1.7233 Steel vs. ACI-ASTM CC50 Steel

Both EN 1.7233 steel and ACI-ASTM CC50 steel are iron alloys. They have 71% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is EN 1.7233 steel and the bottom bar is ACI-ASTM CC50 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210 to 290
210
Elastic (Young's, Tensile) Modulus, GPa 190
200
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 73
80
Tensile Strength: Ultimate (UTS), MPa 700 to 960
430

Thermal Properties

Latent Heat of Fusion, J/g 250
300
Maximum Temperature: Mechanical, °C 430
1100
Melting Completion (Liquidus), °C 1460
1420
Melting Onset (Solidus), °C 1420
1370
Specific Heat Capacity, J/kg-K 470
490
Thermal Conductivity, W/m-K 39
17
Thermal Expansion, µm/m-K 13
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.5
2.7

Otherwise Unclassified Properties

Base Metal Price, % relative 3.0
14
Density, g/cm3 7.8
7.6
Embodied Carbon, kg CO2/kg material 1.6
2.7
Embodied Energy, MJ/kg 21
39
Embodied Water, L/kg 53
170

Common Calculations

PREN (Pitting Resistance) 3.3
28
Stiffness to Weight: Axial, points 13
15
Stiffness to Weight: Bending, points 24
26
Strength to Weight: Axial, points 25 to 34
16
Strength to Weight: Bending, points 22 to 28
17
Thermal Diffusivity, mm2/s 11
4.5
Thermal Shock Resistance, points 21 to 28
14

Alloy Composition

Carbon (C), % 0.39 to 0.45
0 to 0.5
Chromium (Cr), % 1.2 to 1.5
26 to 30
Iron (Fe), % 96.2 to 97.5
62.9 to 74
Manganese (Mn), % 0.4 to 0.7
0 to 1.0
Molybdenum (Mo), % 0.5 to 0.7
0
Nickel (Ni), % 0
0 to 4.0
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 0 to 0.4
0 to 1.5
Sulfur (S), % 0 to 0.035
0 to 0.040