EN 1.7233 Steel vs. ACI-ASTM CN3MN Steel

Both EN 1.7233 steel and ACI-ASTM CN3MN steel are iron alloys. They have 49% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.7233 steel and the bottom bar is ACI-ASTM CN3MN steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210 to 290
180
Elastic (Young's, Tensile) Modulus, GPa 190
210
Elongation at Break, % 18 to 23
39
Fatigue Strength, MPa 270 to 530
250
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
80
Tensile Strength: Ultimate (UTS), MPa 700 to 960
620
Tensile Strength: Yield (Proof), MPa 380 to 780
300

Thermal Properties

Latent Heat of Fusion, J/g 250
310
Maximum Temperature: Mechanical, °C 430
1100
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1410
Specific Heat Capacity, J/kg-K 470
460
Thermal Conductivity, W/m-K 39
13
Thermal Expansion, µm/m-K 13
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
1.8
Electrical Conductivity: Equal Weight (Specific), % IACS 8.5
2.0

Otherwise Unclassified Properties

Base Metal Price, % relative 3.0
33
Density, g/cm3 7.8
8.1
Embodied Carbon, kg CO2/kg material 1.6
6.2
Embodied Energy, MJ/kg 21
84
Embodied Water, L/kg 53
200

Common Calculations

PREN (Pitting Resistance) 3.3
46
Resilience: Ultimate (Unit Rupture Work), MJ/m3 110 to 200
200
Resilience: Unit (Modulus of Resilience), kJ/m3 380 to 1630
210
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 25 to 34
21
Strength to Weight: Bending, points 22 to 28
20
Thermal Diffusivity, mm2/s 11
3.4
Thermal Shock Resistance, points 21 to 28
14

Alloy Composition

Carbon (C), % 0.39 to 0.45
0 to 0.030
Chromium (Cr), % 1.2 to 1.5
20 to 22
Copper (Cu), % 0
0 to 0.75
Iron (Fe), % 96.2 to 97.5
41.4 to 50.3
Manganese (Mn), % 0.4 to 0.7
0 to 2.0
Molybdenum (Mo), % 0.5 to 0.7
6.0 to 7.0
Nickel (Ni), % 0
23.5 to 25.5
Nitrogen (N), % 0
0.18 to 0.26
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 0 to 0.4
0 to 1.0
Sulfur (S), % 0 to 0.035
0 to 0.010