EN 1.7233 Steel vs. ASTM A369 Grade FPB

Both EN 1.7233 steel and ASTM A369 grade FPB are iron alloys. They have a very high 98% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.7233 steel and the bottom bar is ASTM A369 grade FPB.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210 to 290
140
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 18 to 23
19
Fatigue Strength, MPa 270 to 530
180
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 450 to 590
290
Tensile Strength: Ultimate (UTS), MPa 700 to 960
470
Tensile Strength: Yield (Proof), MPa 380 to 780
270

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 430
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 39
52
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 8.5
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 3.0
1.8
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.6
1.4
Embodied Energy, MJ/kg 21
18
Embodied Water, L/kg 53
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110 to 200
78
Resilience: Unit (Modulus of Resilience), kJ/m3 380 to 1630
190
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 25 to 34
17
Strength to Weight: Bending, points 22 to 28
17
Thermal Diffusivity, mm2/s 11
14
Thermal Shock Resistance, points 21 to 28
15

Alloy Composition

Carbon (C), % 0.39 to 0.45
0 to 0.3
Chromium (Cr), % 1.2 to 1.5
0
Iron (Fe), % 96.2 to 97.5
98.1 to 99.61
Manganese (Mn), % 0.4 to 0.7
0.29 to 1.1
Molybdenum (Mo), % 0.5 to 0.7
0
Phosphorus (P), % 0 to 0.025
0 to 0.035
Silicon (Si), % 0 to 0.4
0.1 to 0.5
Sulfur (S), % 0 to 0.035
0 to 0.035