EN 1.7233 Steel vs. EN 1.3518 Steel

Both EN 1.7233 steel and EN 1.3518 steel are iron alloys. Their average alloy composition is basically identical. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is EN 1.7233 steel and the bottom bar is EN 1.3518 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210 to 290
190
Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
72
Tensile Strength: Ultimate (UTS), MPa 700 to 960
630

Thermal Properties

Latent Heat of Fusion, J/g 250
260
Maximum Temperature: Mechanical, °C 430
420
Melting Completion (Liquidus), °C 1460
1440
Melting Onset (Solidus), °C 1420
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 39
43
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.5
8.5

Otherwise Unclassified Properties

Base Metal Price, % relative 3.0
2.4
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.6
1.5
Embodied Energy, MJ/kg 21
20
Embodied Water, L/kg 53
51

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 25 to 34
23
Strength to Weight: Bending, points 22 to 28
21
Thermal Diffusivity, mm2/s 11
12
Thermal Shock Resistance, points 21 to 28
19

Alloy Composition

Aluminum (Al), % 0
0 to 0.050
Carbon (C), % 0.39 to 0.45
0.93 to 1.1
Chromium (Cr), % 1.2 to 1.5
0.9 to 1.2
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 96.2 to 97.5
96.3 to 97.8
Manganese (Mn), % 0.4 to 0.7
0.9 to 1.2
Molybdenum (Mo), % 0.5 to 0.7
0 to 0.1
Oxygen (O), % 0
0 to 0.0015
Phosphorus (P), % 0 to 0.025
0 to 0.025
Silicon (Si), % 0 to 0.4
0.45 to 0.75
Sulfur (S), % 0 to 0.035
0 to 0.030