EN 1.7233 Steel vs. EN 1.3523 Steel

Both EN 1.7233 steel and EN 1.3523 steel are iron alloys. They have a very high 99% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is EN 1.7233 steel and the bottom bar is EN 1.3523 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210 to 290
160 to 220
Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Tensile Strength: Ultimate (UTS), MPa 700 to 960
520 to 1460

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 430
420
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 39
46
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.5
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 3.0
2.3
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.6
1.5
Embodied Energy, MJ/kg 21
19
Embodied Water, L/kg 53
53

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 25 to 34
19 to 52
Strength to Weight: Bending, points 22 to 28
18 to 36
Thermal Diffusivity, mm2/s 11
12
Thermal Shock Resistance, points 21 to 28
15 to 42

Alloy Composition

Aluminum (Al), % 0
0 to 0.050
Carbon (C), % 0.39 to 0.45
0.17 to 0.22
Chromium (Cr), % 1.2 to 1.5
1.0 to 1.3
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 96.2 to 97.5
96.5 to 97.9
Manganese (Mn), % 0.4 to 0.7
1.1 to 1.4
Molybdenum (Mo), % 0.5 to 0.7
0
Oxygen (O), % 0
0 to 0.0020
Phosphorus (P), % 0 to 0.025
0 to 0.025
Silicon (Si), % 0 to 0.4
0 to 0.4
Sulfur (S), % 0 to 0.035
0 to 0.030

Comparable Variants