EN 1.7233 Steel vs. EN 1.4317 Stainless Steel

Both EN 1.7233 steel and EN 1.4317 stainless steel are iron alloys. They have 84% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.7233 steel and the bottom bar is EN 1.4317 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 18 to 23
17
Fatigue Strength, MPa 270 to 530
380
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
76
Tensile Strength: Ultimate (UTS), MPa 700 to 960
860
Tensile Strength: Yield (Proof), MPa 380 to 780
630

Thermal Properties

Latent Heat of Fusion, J/g 250
280
Maximum Temperature: Mechanical, °C 430
770
Melting Completion (Liquidus), °C 1460
1440
Melting Onset (Solidus), °C 1420
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 39
26
Thermal Expansion, µm/m-K 13
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
2.7
Electrical Conductivity: Equal Weight (Specific), % IACS 8.5
3.2

Otherwise Unclassified Properties

Base Metal Price, % relative 3.0
10
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.6
2.4
Embodied Energy, MJ/kg 21
33
Embodied Water, L/kg 53
110

Common Calculations

PREN (Pitting Resistance) 3.3
14
Resilience: Ultimate (Unit Rupture Work), MJ/m3 110 to 200
130
Resilience: Unit (Modulus of Resilience), kJ/m3 380 to 1630
1010
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 25 to 34
31
Strength to Weight: Bending, points 22 to 28
26
Thermal Diffusivity, mm2/s 11
7.0
Thermal Shock Resistance, points 21 to 28
30

Alloy Composition

Carbon (C), % 0.39 to 0.45
0 to 0.060
Chromium (Cr), % 1.2 to 1.5
12 to 13.5
Iron (Fe), % 96.2 to 97.5
78.7 to 84.5
Manganese (Mn), % 0.4 to 0.7
0 to 1.0
Molybdenum (Mo), % 0.5 to 0.7
0 to 0.7
Nickel (Ni), % 0
3.5 to 5.0
Phosphorus (P), % 0 to 0.025
0 to 0.035
Silicon (Si), % 0 to 0.4
0 to 1.0
Sulfur (S), % 0 to 0.035
0 to 0.025