EN 1.7233 Steel vs. R30816 Cobalt

EN 1.7233 steel belongs to the iron alloys classification, while R30816 cobalt belongs to the cobalt alloys. There are 26 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is EN 1.7233 steel and the bottom bar is R30816 cobalt.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210 to 290
280
Elastic (Young's, Tensile) Modulus, GPa 190
210
Elongation at Break, % 18 to 23
23
Fatigue Strength, MPa 270 to 530
250
Poisson's Ratio 0.29
0.3
Shear Modulus, GPa 73
81
Tensile Strength: Ultimate (UTS), MPa 700 to 960
1020
Tensile Strength: Yield (Proof), MPa 380 to 780
460

Thermal Properties

Latent Heat of Fusion, J/g 250
300
Melting Completion (Liquidus), °C 1460
1540
Melting Onset (Solidus), °C 1420
1460
Specific Heat Capacity, J/kg-K 470
420
Thermal Conductivity, W/m-K 39
13
Thermal Expansion, µm/m-K 13
12

Otherwise Unclassified Properties

Density, g/cm3 7.8
9.1
Embodied Carbon, kg CO2/kg material 1.6
20
Embodied Energy, MJ/kg 21
320
Embodied Water, L/kg 53
440

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110 to 200
190
Resilience: Unit (Modulus of Resilience), kJ/m3 380 to 1630
510
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
22
Strength to Weight: Axial, points 25 to 34
31
Strength to Weight: Bending, points 22 to 28
25
Thermal Diffusivity, mm2/s 11
3.3
Thermal Shock Resistance, points 21 to 28
28

Alloy Composition

Carbon (C), % 0.39 to 0.45
0.32 to 0.42
Chromium (Cr), % 1.2 to 1.5
19 to 21
Cobalt (Co), % 0
40 to 49.8
Iron (Fe), % 96.2 to 97.5
0 to 5.0
Manganese (Mn), % 0.4 to 0.7
1.0 to 2.0
Molybdenum (Mo), % 0.5 to 0.7
3.5 to 4.5
Nickel (Ni), % 0
19 to 21
Niobium (Nb), % 0
3.5 to 4.5
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 0 to 0.4
0 to 1.0
Sulfur (S), % 0 to 0.035
0 to 0.030
Tantalum (Ta), % 0
3.5 to 4.5
Tungsten (W), % 0
3.5 to 4.5