EN 1.7233 Steel vs. S13800 Stainless Steel

Both EN 1.7233 steel and S13800 stainless steel are iron alloys. They have 78% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.7233 steel and the bottom bar is S13800 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210 to 290
290 to 480
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 18 to 23
11 to 18
Fatigue Strength, MPa 270 to 530
410 to 870
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
77
Shear Strength, MPa 450 to 590
610 to 1030
Tensile Strength: Ultimate (UTS), MPa 700 to 960
980 to 1730
Tensile Strength: Yield (Proof), MPa 380 to 780
660 to 1580

Thermal Properties

Latent Heat of Fusion, J/g 250
280
Maximum Temperature: Mechanical, °C 430
810
Melting Completion (Liquidus), °C 1460
1450
Melting Onset (Solidus), °C 1420
1410
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 39
16
Thermal Expansion, µm/m-K 13
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.5
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 3.0
15
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.6
3.4
Embodied Energy, MJ/kg 21
46
Embodied Water, L/kg 53
140

Common Calculations

PREN (Pitting Resistance) 3.3
21
Resilience: Ultimate (Unit Rupture Work), MJ/m3 110 to 200
150 to 190
Resilience: Unit (Modulus of Resilience), kJ/m3 380 to 1630
1090 to 5490
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 25 to 34
35 to 61
Strength to Weight: Bending, points 22 to 28
28 to 41
Thermal Diffusivity, mm2/s 11
4.3
Thermal Shock Resistance, points 21 to 28
33 to 58

Alloy Composition

Aluminum (Al), % 0
0.9 to 1.4
Carbon (C), % 0.39 to 0.45
0 to 0.050
Chromium (Cr), % 1.2 to 1.5
12.3 to 13.2
Iron (Fe), % 96.2 to 97.5
73.6 to 77.3
Manganese (Mn), % 0.4 to 0.7
0 to 0.2
Molybdenum (Mo), % 0.5 to 0.7
2.0 to 3.0
Nickel (Ni), % 0
7.5 to 8.5
Nitrogen (N), % 0
0 to 0.010
Phosphorus (P), % 0 to 0.025
0 to 0.010
Silicon (Si), % 0 to 0.4
0 to 0.1
Sulfur (S), % 0 to 0.035
0 to 0.0080