EN 1.7233 Steel vs. S35140 Stainless Steel

Both EN 1.7233 steel and S35140 stainless steel are iron alloys. They have 51% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.7233 steel and the bottom bar is S35140 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210 to 290
210
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 18 to 23
34
Fatigue Strength, MPa 270 to 530
250
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
78
Shear Strength, MPa 450 to 590
460
Tensile Strength: Ultimate (UTS), MPa 700 to 960
690
Tensile Strength: Yield (Proof), MPa 380 to 780
310

Thermal Properties

Latent Heat of Fusion, J/g 250
300
Maximum Temperature: Mechanical, °C 430
1100
Melting Completion (Liquidus), °C 1460
1420
Melting Onset (Solidus), °C 1420
1370
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 39
14
Thermal Expansion, µm/m-K 13
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 8.5
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 3.0
31
Density, g/cm3 7.8
8.0
Embodied Carbon, kg CO2/kg material 1.6
5.5
Embodied Energy, MJ/kg 21
78
Embodied Water, L/kg 53
190

Common Calculations

PREN (Pitting Resistance) 3.3
28
Resilience: Ultimate (Unit Rupture Work), MJ/m3 110 to 200
190
Resilience: Unit (Modulus of Resilience), kJ/m3 380 to 1630
250
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 25 to 34
24
Strength to Weight: Bending, points 22 to 28
22
Thermal Diffusivity, mm2/s 11
3.7
Thermal Shock Resistance, points 21 to 28
16

Alloy Composition

Carbon (C), % 0.39 to 0.45
0 to 0.1
Chromium (Cr), % 1.2 to 1.5
20 to 22
Iron (Fe), % 96.2 to 97.5
44.1 to 52.7
Manganese (Mn), % 0.4 to 0.7
1.0 to 3.0
Molybdenum (Mo), % 0.5 to 0.7
1.0 to 2.0
Nickel (Ni), % 0
25 to 27
Niobium (Nb), % 0
0.25 to 0.75
Nitrogen (N), % 0
0.080 to 0.2
Phosphorus (P), % 0 to 0.025
0 to 0.045
Silicon (Si), % 0 to 0.4
0 to 0.75
Sulfur (S), % 0 to 0.035
0 to 0.030