EN 1.7240 Steel vs. SAE-AISI 4140 Steel

Both EN 1.7240 steel and SAE-AISI 4140 steel are iron alloys. Their average alloy composition is basically identical. There are 25 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is EN 1.7240 steel and the bottom bar is SAE-AISI 4140 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200 to 480
200 to 310
Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Tensile Strength: Ultimate (UTS), MPa 670 to 1990
690 to 1080

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 420
420
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1410
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 44
43
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 2.4
2.4
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.5
1.5
Embodied Energy, MJ/kg 20
20
Embodied Water, L/kg 50
51

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 24 to 71
25 to 38
Strength to Weight: Bending, points 22 to 45
22 to 30
Thermal Diffusivity, mm2/s 12
12
Thermal Shock Resistance, points 20 to 59
20 to 32

Alloy Composition

Carbon (C), % 0.56 to 0.64
0.38 to 0.43
Chromium (Cr), % 0.7 to 1.0
0.8 to 1.1
Iron (Fe), % 96.7 to 97.9
96.8 to 97.8
Manganese (Mn), % 0.7 to 1.0
0.75 to 1.0
Molybdenum (Mo), % 0.15 to 0.25
0.15 to 0.25
Phosphorus (P), % 0 to 0.025
0 to 0.035
Silicon (Si), % 0 to 0.4
0.15 to 0.35
Sulfur (S), % 0 to 0.025
0 to 0.040

Comparable Variants