EN 1.7240 Steel vs. N06035 Nickel

EN 1.7240 steel belongs to the iron alloys classification, while N06035 nickel belongs to the nickel alloys. There are 20 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is EN 1.7240 steel and the bottom bar is N06035 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
210
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
84
Tensile Strength: Ultimate (UTS), MPa 670 to 1990
660

Thermal Properties

Latent Heat of Fusion, J/g 250
340
Maximum Temperature: Mechanical, °C 420
1030
Melting Completion (Liquidus), °C 1460
1440
Melting Onset (Solidus), °C 1410
1390
Specific Heat Capacity, J/kg-K 470
450
Thermal Expansion, µm/m-K 13
13

Otherwise Unclassified Properties

Base Metal Price, % relative 2.4
60
Density, g/cm3 7.8
8.4
Embodied Carbon, kg CO2/kg material 1.5
10
Embodied Energy, MJ/kg 20
140
Embodied Water, L/kg 50
330

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 24 to 71
22
Strength to Weight: Bending, points 22 to 45
20
Thermal Shock Resistance, points 20 to 59
17

Alloy Composition

Aluminum (Al), % 0
0 to 0.4
Carbon (C), % 0.56 to 0.64
0 to 0.050
Chromium (Cr), % 0.7 to 1.0
32.3 to 34.3
Cobalt (Co), % 0
0 to 1.0
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 96.7 to 97.9
0 to 2.0
Manganese (Mn), % 0.7 to 1.0
0 to 0.5
Molybdenum (Mo), % 0.15 to 0.25
7.6 to 9.0
Nickel (Ni), % 0
51.1 to 60.2
Phosphorus (P), % 0 to 0.025
0 to 0.030
Silicon (Si), % 0 to 0.4
0 to 0.6
Sulfur (S), % 0 to 0.025
0 to 0.015
Tungsten (W), % 0
0 to 0.6
Vanadium (V), % 0
0 to 0.2