MakeItFrom.com
Menu (ESC)

EN 1.7323 Steel vs. ASTM A369 Grade FP22

Both EN 1.7323 steel and ASTM A369 grade FP22 are iron alloys. They have a very high 98% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is EN 1.7323 steel and the bottom bar is ASTM A369 grade FP22.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150 to 180
140
Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
74
Tensile Strength: Ultimate (UTS), MPa 480 to 1460
470

Thermal Properties

Latent Heat of Fusion, J/g 250
260
Maximum Temperature: Mechanical, °C 410
460
Melting Completion (Liquidus), °C 1460
1470
Melting Onset (Solidus), °C 1420
1430
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 45
39
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
7.6
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
8.7

Otherwise Unclassified Properties

Base Metal Price, % relative 2.5
3.8
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 1.5
1.7
Embodied Energy, MJ/kg 20
23
Embodied Water, L/kg 50
58

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 17 to 52
17
Strength to Weight: Bending, points 17 to 36
17
Thermal Diffusivity, mm2/s 12
11
Thermal Shock Resistance, points 14 to 43
14

Alloy Composition

Carbon (C), % 0.17 to 0.23
0.050 to 0.15
Chromium (Cr), % 0.3 to 0.6
1.9 to 2.6
Copper (Cu), % 0 to 0.25
0
Iron (Fe), % 97.1 to 98.4
95 to 96.9
Manganese (Mn), % 0.7 to 1.0
0.3 to 0.6
Molybdenum (Mo), % 0.4 to 0.5
0.87 to 1.1
Phosphorus (P), % 0 to 0.025
0 to 0.025
Silicon (Si), % 0 to 0.3
0 to 0.5
Sulfur (S), % 0.020 to 0.040
0 to 0.025