EN 1.7365 Steel vs. EN 1.1118 Cast Steel

Both EN 1.7365 steel and EN 1.1118 cast steel are iron alloys. They have a moderately high 94% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.7365 steel and the bottom bar is EN 1.1118 cast steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 18
14 to 21
Fatigue Strength, MPa 320
320 to 400
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 74
73
Tensile Strength: Ultimate (UTS), MPa 700
700 to 750
Tensile Strength: Yield (Proof), MPa 470
460 to 630

Thermal Properties

Latent Heat of Fusion, J/g 260
250
Maximum Temperature: Mechanical, °C 510
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 40
51
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 8.2
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 9.4
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 4.4
1.9
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.8
1.4
Embodied Energy, MJ/kg 24
19
Embodied Water, L/kg 70
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
97 to 130
Resilience: Unit (Modulus of Resilience), kJ/m3 580
550 to 1050
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 25
25 to 27
Strength to Weight: Bending, points 22
22 to 23
Thermal Diffusivity, mm2/s 11
14
Thermal Shock Resistance, points 20
22 to 24

Alloy Composition

Carbon (C), % 0.12 to 0.19
0.2 to 0.25
Chromium (Cr), % 4.0 to 6.0
0
Copper (Cu), % 0 to 0.3
0
Iron (Fe), % 91.2 to 94.9
97.3 to 98.3
Manganese (Mn), % 0.5 to 0.8
1.5 to 1.8
Molybdenum (Mo), % 0.45 to 0.65
0
Phosphorus (P), % 0 to 0.025
0 to 0.020
Silicon (Si), % 0 to 0.8
0 to 0.6
Sulfur (S), % 0 to 0.025
0 to 0.015
Vanadium (V), % 0 to 0.050
0