EN 1.7367 Steel vs. SAE-AISI 1015 Steel

Both EN 1.7367 steel and SAE-AISI 1015 steel are iron alloys. They have 89% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.7367 steel and the bottom bar is SAE-AISI 1015 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200
120
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 18
20 to 32
Fatigue Strength, MPa 310
170 to 250
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 75
73
Tensile Strength: Ultimate (UTS), MPa 670
390 to 440
Tensile Strength: Yield (Proof), MPa 460
210 to 370

Thermal Properties

Latent Heat of Fusion, J/g 270
250
Maximum Temperature: Mechanical, °C 600
400
Melting Completion (Liquidus), °C 1460
1470
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 26
52
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 8.9
6.9
Electrical Conductivity: Equal Weight (Specific), % IACS 10
7.9

Otherwise Unclassified Properties

Base Metal Price, % relative 7.0
1.8
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 2.6
1.4
Embodied Energy, MJ/kg 37
18
Embodied Water, L/kg 88
45

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
83 to 110
Resilience: Unit (Modulus of Resilience), kJ/m3 560
120 to 360
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 24
14 to 15
Strength to Weight: Bending, points 22
15 to 16
Thermal Diffusivity, mm2/s 6.9
14
Thermal Shock Resistance, points 19
12 to 14

Alloy Composition

Aluminum (Al), % 0 to 0.020
0
Carbon (C), % 0.080 to 0.12
0.13 to 0.18
Chromium (Cr), % 8.0 to 9.5
0
Iron (Fe), % 87.3 to 90.3
99.13 to 99.57
Manganese (Mn), % 0.3 to 0.6
0.3 to 0.6
Molybdenum (Mo), % 0.85 to 1.1
0
Nickel (Ni), % 0 to 0.4
0
Niobium (Nb), % 0.060 to 0.1
0
Nitrogen (N), % 0.030 to 0.070
0
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0.2 to 0.5
0
Sulfur (S), % 0 to 0.010
0 to 0.050
Titanium (Ti), % 0 to 0.010
0
Vanadium (V), % 0.18 to 0.25
0
Zirconium (Zr), % 0 to 0.010
0