EN 1.7380 Steel vs. ASTM B617 Coin Silver

EN 1.7380 steel belongs to the iron alloys classification, while ASTM B617 coin silver belongs to the otherwise unclassified metals. There are 19 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.

For each property being compared, the top bar is EN 1.7380 steel and the bottom bar is ASTM B617 coin silver.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
75
Elongation at Break, % 19 to 20
1.1 to 22
Poisson's Ratio 0.29
0.37
Shear Modulus, GPa 74
28
Shear Strength, MPa 330 to 350
180 to 290
Tensile Strength: Ultimate (UTS), MPa 540 to 550
290 to 520

Thermal Properties

Latent Heat of Fusion, J/g 260
120
Melting Completion (Liquidus), °C 1470
870
Melting Onset (Solidus), °C 1430
780
Specific Heat Capacity, J/kg-K 470
250
Thermal Expansion, µm/m-K 13
19

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.6
83
Electrical Conductivity: Equal Weight (Specific), % IACS 8.7
72

Otherwise Unclassified Properties

Density, g/cm3 7.9
10

Common Calculations

Stiffness to Weight: Axial, points 13
4.1
Stiffness to Weight: Bending, points 24
14
Strength to Weight: Axial, points 19 to 20
7.7 to 14
Strength to Weight: Bending, points 19
9.3 to 14
Thermal Shock Resistance, points 15 to 16
14 to 25

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
0 to 0.0050
Cadmium (Cd), % 0
0 to 0.050
Carbon (C), % 0.080 to 0.14
0
Chromium (Cr), % 2.0 to 2.5
0
Copper (Cu), % 0 to 0.3
9.0 to 10.4
Iron (Fe), % 94.6 to 96.6
0 to 0.050
Lead (Pb), % 0
0 to 0.030
Manganese (Mn), % 0.4 to 0.8
0
Molybdenum (Mo), % 0.9 to 1.1
0
Nickel (Ni), % 0
0 to 0.010
Nitrogen (N), % 0 to 0.012
0
Phosphorus (P), % 0 to 0.020
0 to 0.020
Silicon (Si), % 0 to 0.5
0
Silver (Ag), % 0
89.6 to 91
Sulfur (S), % 0 to 0.010
0
Zinc (Zn), % 0
0 to 0.060
Residuals, % 0
0 to 0.060