EN 1.7380 Steel vs. ASTM B780 Alloy

EN 1.7380 steel belongs to the iron alloys classification, while ASTM B780 alloy belongs to the otherwise unclassified metals. There are 17 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.

For each property being compared, the top bar is EN 1.7380 steel and the bottom bar is ASTM B780 alloy.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
83
Elongation at Break, % 19 to 20
1.1 to 9.1
Poisson's Ratio 0.29
0.36
Shear Modulus, GPa 74
30
Shear Strength, MPa 330 to 350
200 to 340
Tensile Strength: Ultimate (UTS), MPa 540 to 550
330 to 590

Thermal Properties

Latent Heat of Fusion, J/g 260
140
Specific Heat Capacity, J/kg-K 470
270
Thermal Expansion, µm/m-K 13
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.6
70 to 76
Electrical Conductivity: Equal Weight (Specific), % IACS 8.7
62 to 68

Otherwise Unclassified Properties

Density, g/cm3 7.9
10

Common Calculations

Stiffness to Weight: Axial, points 13
4.5
Stiffness to Weight: Bending, points 24
14
Strength to Weight: Axial, points 19 to 20
9.1 to 16
Strength to Weight: Bending, points 19
11 to 15
Thermal Shock Resistance, points 15 to 16
16 to 29

Alloy Composition

Cadmium (Cd), % 0
0 to 0.050
Carbon (C), % 0.080 to 0.14
0
Chromium (Cr), % 2.0 to 2.5
0
Copper (Cu), % 0 to 0.3
23.5 to 25.7
Iron (Fe), % 94.6 to 96.6
0 to 0.050
Lead (Pb), % 0
0 to 0.030
Manganese (Mn), % 0.4 to 0.8
0
Molybdenum (Mo), % 0.9 to 1.1
0
Nickel (Ni), % 0
0.35 to 0.65
Nitrogen (N), % 0 to 0.012
0
Phosphorus (P), % 0 to 0.020
0
Silicon (Si), % 0 to 0.5
0
Silver (Ag), % 0
74 to 76
Sulfur (S), % 0 to 0.010
0
Zinc (Zn), % 0
0 to 0.060