EN 1.7380 Steel vs. EN 1.1121 Steel

Both EN 1.7380 steel and EN 1.1121 steel are iron alloys. They have a very high 96% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.7380 steel and the bottom bar is EN 1.1121 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160 to 170
120
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 19 to 20
28
Fatigue Strength, MPa 200 to 230
160
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 74
73
Shear Strength, MPa 330 to 350
260
Tensile Strength: Ultimate (UTS), MPa 540 to 550
400
Tensile Strength: Yield (Proof), MPa 290 to 330
210

Thermal Properties

Latent Heat of Fusion, J/g 260
250
Maximum Temperature: Mechanical, °C 460
400
Melting Completion (Liquidus), °C 1470
1460
Melting Onset (Solidus), °C 1430
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 39
53
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.6
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 8.7
8.0

Otherwise Unclassified Properties

Base Metal Price, % relative 3.8
1.8
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 1.8
1.4
Embodied Energy, MJ/kg 23
18
Embodied Water, L/kg 59
45

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 87 to 98
93
Resilience: Unit (Modulus of Resilience), kJ/m3 230 to 280
110
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 19 to 20
14
Strength to Weight: Bending, points 19
15
Thermal Diffusivity, mm2/s 11
14
Thermal Shock Resistance, points 15 to 16
13

Alloy Composition

Carbon (C), % 0.080 to 0.14
0.070 to 0.13
Chromium (Cr), % 2.0 to 2.5
0
Copper (Cu), % 0 to 0.3
0
Iron (Fe), % 94.6 to 96.6
98.8 to 99.63
Manganese (Mn), % 0.4 to 0.8
0.3 to 0.6
Molybdenum (Mo), % 0.9 to 1.1
0
Nitrogen (N), % 0 to 0.012
0
Phosphorus (P), % 0 to 0.020
0 to 0.035
Silicon (Si), % 0 to 0.5
0 to 0.4
Sulfur (S), % 0 to 0.010
0 to 0.035