EN 1.7380 Steel vs. EN 1.3553 Steel

Both EN 1.7380 steel and EN 1.3553 steel are iron alloys. They have 86% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is EN 1.7380 steel and the bottom bar is EN 1.3553 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160 to 170
220
Elastic (Young's, Tensile) Modulus, GPa 190
200
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 74
77
Tensile Strength: Ultimate (UTS), MPa 540 to 550
720

Thermal Properties

Latent Heat of Fusion, J/g 260
260
Maximum Temperature: Mechanical, °C 460
540
Melting Completion (Liquidus), °C 1470
1620
Melting Onset (Solidus), °C 1430
1570
Specific Heat Capacity, J/kg-K 470
440
Thermal Conductivity, W/m-K 39
24
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.6
10
Electrical Conductivity: Equal Weight (Specific), % IACS 8.7
11

Otherwise Unclassified Properties

Base Metal Price, % relative 3.8
24
Density, g/cm3 7.9
8.4
Embodied Carbon, kg CO2/kg material 1.8
8.5
Embodied Energy, MJ/kg 23
130
Embodied Water, L/kg 59
96

Common Calculations

PREN (Pitting Resistance) 5.6
31
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
23
Strength to Weight: Axial, points 19 to 20
24
Strength to Weight: Bending, points 19
21
Thermal Diffusivity, mm2/s 11
6.4
Thermal Shock Resistance, points 15 to 16
21

Alloy Composition

Carbon (C), % 0.080 to 0.14
0.78 to 0.86
Chromium (Cr), % 2.0 to 2.5
3.9 to 4.3
Copper (Cu), % 0 to 0.3
0 to 0.3
Iron (Fe), % 94.6 to 96.6
80.7 to 83.7
Manganese (Mn), % 0.4 to 0.8
0 to 0.4
Molybdenum (Mo), % 0.9 to 1.1
4.7 to 5.2
Nitrogen (N), % 0 to 0.012
0
Phosphorus (P), % 0 to 0.020
0 to 0.025
Silicon (Si), % 0 to 0.5
0 to 0.4
Sulfur (S), % 0 to 0.010
0 to 0.015
Tungsten (W), % 0
6.0 to 6.7
Vanadium (V), % 0
1.7 to 2.0