EN 1.7380 Steel vs. EN 1.5522 Steel

Both EN 1.7380 steel and EN 1.5522 steel are iron alloys. They have a very high 97% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.7380 steel and the bottom bar is EN 1.5522 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160 to 170
140 to 190
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 19 to 20
11 to 21
Fatigue Strength, MPa 200 to 230
210 to 330
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 74
73
Shear Strength, MPa 330 to 350
320 to 380
Tensile Strength: Ultimate (UTS), MPa 540 to 550
450 to 1490
Tensile Strength: Yield (Proof), MPa 290 to 330
300 to 520

Thermal Properties

Latent Heat of Fusion, J/g 260
250
Maximum Temperature: Mechanical, °C 460
400
Melting Completion (Liquidus), °C 1470
1460
Melting Onset (Solidus), °C 1430
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 39
51
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.6
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 8.7
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 3.8
1.9
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 1.8
1.4
Embodied Energy, MJ/kg 23
19
Embodied Water, L/kg 59
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 87 to 98
45 to 250
Resilience: Unit (Modulus of Resilience), kJ/m3 230 to 280
250 to 720
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 19 to 20
16 to 53
Strength to Weight: Bending, points 19
17 to 37
Thermal Diffusivity, mm2/s 11
14
Thermal Shock Resistance, points 15 to 16
13 to 44

Alloy Composition

Boron (B), % 0
0.00080 to 0.0050
Carbon (C), % 0.080 to 0.14
0.2 to 0.24
Chromium (Cr), % 2.0 to 2.5
0
Copper (Cu), % 0 to 0.3
0 to 0.25
Iron (Fe), % 94.6 to 96.6
98 to 98.9
Manganese (Mn), % 0.4 to 0.8
0.9 to 1.2
Molybdenum (Mo), % 0.9 to 1.1
0
Nitrogen (N), % 0 to 0.012
0
Phosphorus (P), % 0 to 0.020
0 to 0.025
Silicon (Si), % 0 to 0.5
0 to 0.3
Sulfur (S), % 0 to 0.010
0 to 0.025