EN 1.7380 Steel vs. EN 1.7033 Steel
Both EN 1.7380 steel and EN 1.7033 steel are iron alloys. They have a very high 98% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is EN 1.7380 steel and the bottom bar is EN 1.7033 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 160 to 170 | |
| 150 to 240 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 74 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 540 to 550 | |
| 500 to 1720 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 460 | |
| 420 |
| Melting Completion (Liquidus), °C | 1470 | |
| 1460 |
| Melting Onset (Solidus), °C | 1430 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 39 | |
| 45 |
| Thermal Expansion, µm/m-K | 13 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.6 | |
| 7.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.7 | |
| 8.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 3.8 | |
| 2.2 |
| Density, g/cm3 | 7.9 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.8 | |
| 1.4 |
| Embodied Energy, MJ/kg | 23 | |
| 19 |
| Embodied Water, L/kg | 59 | |
| 50 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 19 to 20 | |
| 18 to 61 |
| Strength to Weight: Bending, points | 19 | |
| 18 to 41 |
| Thermal Diffusivity, mm2/s | 11 | |
| 12 |
| Thermal Shock Resistance, points | 15 to 16 | |
| 15 to 50 |
Alloy Composition
| Carbon (C), % | 0.080 to 0.14 | |
| 0.3 to 0.37 |
| Chromium (Cr), % | 2.0 to 2.5 | |
| 0.9 to 1.2 |
| Copper (Cu), % | 0 to 0.3 | |
| 0 |
| Iron (Fe), % | 94.6 to 96.6 | |
| 97.1 to 98.2 |
| Manganese (Mn), % | 0.4 to 0.8 | |
| 0.6 to 0.9 |
| Molybdenum (Mo), % | 0.9 to 1.1 | |
| 0 |
| Nitrogen (N), % | 0 to 0.012 | |
| 0 |
| Phosphorus (P), % | 0 to 0.020 | |
| 0 to 0.035 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 to 0.4 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 to 0.035 |