EN 1.7380 Steel vs. EN 1.8152 Steel

Both EN 1.7380 steel and EN 1.8152 steel are iron alloys. They have a very high 97% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is EN 1.7380 steel and the bottom bar is EN 1.8152 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160 to 170
200 to 540
Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 74
72
Tensile Strength: Ultimate (UTS), MPa 540 to 550
660 to 2010

Thermal Properties

Latent Heat of Fusion, J/g 260
270
Maximum Temperature: Mechanical, °C 460
410
Melting Completion (Liquidus), °C 1470
1440
Melting Onset (Solidus), °C 1430
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 39
47
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.6
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 8.7
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 3.8
2.2
Density, g/cm3 7.9
7.7
Embodied Carbon, kg CO2/kg material 1.8
1.8
Embodied Energy, MJ/kg 23
25
Embodied Water, L/kg 59
49

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 19 to 20
24 to 72
Strength to Weight: Bending, points 19
22 to 46
Thermal Diffusivity, mm2/s 11
13
Thermal Shock Resistance, points 15 to 16
20 to 60

Alloy Composition

Carbon (C), % 0.080 to 0.14
0.51 to 0.59
Chromium (Cr), % 2.0 to 2.5
0.5 to 0.8
Copper (Cu), % 0 to 0.3
0
Iron (Fe), % 94.6 to 96.6
96 to 97.2
Manganese (Mn), % 0.4 to 0.8
0.5 to 0.8
Molybdenum (Mo), % 0.9 to 1.1
0
Nitrogen (N), % 0 to 0.012
0
Phosphorus (P), % 0 to 0.020
0 to 0.025
Silicon (Si), % 0 to 0.5
1.2 to 1.6
Sulfur (S), % 0 to 0.010
0 to 0.025
Vanadium (V), % 0
0.1 to 0.2

Comparable Variants