EN 1.7380 Steel vs. Grade CU5MCuC Nickel
EN 1.7380 steel belongs to the iron alloys classification, while grade CU5MCuC nickel belongs to the nickel alloys. They have a modest 34% of their average alloy composition in common, which, by itself, doesn't mean much. There are 26 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is EN 1.7380 steel and the bottom bar is grade CU5MCuC nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Elongation at Break, % | 19 to 20 | |
| 22 |
| Fatigue Strength, MPa | 200 to 230 | |
| 170 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 74 | |
| 77 |
| Tensile Strength: Ultimate (UTS), MPa | 540 to 550 | |
| 580 |
| Tensile Strength: Yield (Proof), MPa | 290 to 330 | |
| 270 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 310 |
| Maximum Temperature: Mechanical, °C | 460 | |
| 980 |
| Melting Completion (Liquidus), °C | 1470 | |
| 1420 |
| Melting Onset (Solidus), °C | 1430 | |
| 1370 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 460 |
| Thermal Expansion, µm/m-K | 13 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 3.8 | |
| 45 |
| Density, g/cm3 | 7.9 | |
| 8.2 |
| Embodied Carbon, kg CO2/kg material | 1.8 | |
| 7.7 |
| Embodied Energy, MJ/kg | 23 | |
| 110 |
| Embodied Water, L/kg | 59 | |
| 230 |
Common Calculations
| PREN (Pitting Resistance) | 5.6 | |
| 31 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 87 to 98 | |
| 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 230 to 280 | |
| 190 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 19 to 20 | |
| 20 |
| Strength to Weight: Bending, points | 19 | |
| 19 |
| Thermal Shock Resistance, points | 15 to 16 | |
| 16 |
Alloy Composition
| Carbon (C), % | 0.080 to 0.14 | |
| 0 to 0.050 |
| Chromium (Cr), % | 2.0 to 2.5 | |
| 19.5 to 23.5 |
| Copper (Cu), % | 0 to 0.3 | |
| 1.5 to 3.5 |
| Iron (Fe), % | 94.6 to 96.6 | |
| 22.2 to 37.9 |
| Manganese (Mn), % | 0.4 to 0.8 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 0.9 to 1.1 | |
| 2.5 to 3.5 |
| Nickel (Ni), % | 0 | |
| 38 to 44 |
| Niobium (Nb), % | 0 | |
| 0.6 to 1.2 |
| Nitrogen (N), % | 0 to 0.012 | |
| 0 |
| Phosphorus (P), % | 0 to 0.020 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 to 0.030 |