EN 1.7380 Steel vs. Grade FDSiCr Steel

Both EN 1.7380 steel and grade FDSiCr steel are iron alloys. They have a very high 97% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is EN 1.7380 steel and the bottom bar is grade FDSiCr steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160 to 170
580
Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 74
80
Tensile Strength: Ultimate (UTS), MPa 540 to 550
1930

Thermal Properties

Latent Heat of Fusion, J/g 260
270
Maximum Temperature: Mechanical, °C 460
410
Melting Completion (Liquidus), °C 1470
1440
Melting Onset (Solidus), °C 1430
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 39
48
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.6
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.7
8.5

Otherwise Unclassified Properties

Base Metal Price, % relative 3.8
2.2
Density, g/cm3 7.9
7.7
Embodied Carbon, kg CO2/kg material 1.8
1.5
Embodied Energy, MJ/kg 23
20
Embodied Water, L/kg 59
48

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 19 to 20
69
Strength to Weight: Bending, points 19
44
Thermal Diffusivity, mm2/s 11
13
Thermal Shock Resistance, points 15 to 16
58

Alloy Composition

Carbon (C), % 0.080 to 0.14
0.5 to 0.6
Chromium (Cr), % 2.0 to 2.5
0.5 to 0.8
Copper (Cu), % 0 to 0.3
0 to 0.12
Iron (Fe), % 94.6 to 96.6
96.5 to 97.8
Manganese (Mn), % 0.4 to 0.8
0.5 to 0.9
Molybdenum (Mo), % 0.9 to 1.1
0
Nitrogen (N), % 0 to 0.012
0
Phosphorus (P), % 0 to 0.020
0 to 0.030
Silicon (Si), % 0 to 0.5
1.2 to 1.6
Sulfur (S), % 0 to 0.010
0 to 0.025