EN 1.7380 Steel vs. Solder Alloy 161

EN 1.7380 steel belongs to the iron alloys classification, while solder alloy 161 belongs to the otherwise unclassified metals. There are 23 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is EN 1.7380 steel and the bottom bar is solder alloy 161.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
38
Elongation at Break, % 19 to 20
44
Poisson's Ratio 0.29
0.39
Shear Modulus, GPa 74
14
Tensile Strength: Ultimate (UTS), MPa 540 to 550
53

Thermal Properties

Latent Heat of Fusion, J/g 260
48
Melting Completion (Liquidus), °C 1470
190
Melting Onset (Solidus), °C 1430
180
Specific Heat Capacity, J/kg-K 470
190
Thermal Conductivity, W/m-K 39
49
Thermal Expansion, µm/m-K 13
25

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.6
11
Electrical Conductivity: Equal Weight (Specific), % IACS 8.7
11

Otherwise Unclassified Properties

Density, g/cm3 7.9
8.9
Embodied Carbon, kg CO2/kg material 1.8
11
Embodied Energy, MJ/kg 23
180
Embodied Water, L/kg 59
910

Common Calculations

Stiffness to Weight: Axial, points 13
2.4
Stiffness to Weight: Bending, points 24
13
Strength to Weight: Axial, points 19 to 20
1.7
Strength to Weight: Bending, points 19
3.5
Thermal Diffusivity, mm2/s 11
29
Thermal Shock Resistance, points 15 to 16
4.1

Alloy Composition

Aluminum (Al), % 0
0 to 0.0010
Antimony (Sb), % 0
0 to 0.2
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.1
Cadmium (Cd), % 0
0 to 0.0020
Carbon (C), % 0.080 to 0.14
0
Chromium (Cr), % 2.0 to 2.5
0
Copper (Cu), % 0 to 0.3
1.2 to 1.6
Gold (Au), % 0
0 to 0.050
Indium (In), % 0
0 to 0.1
Iron (Fe), % 94.6 to 96.6
0 to 0.020
Lead (Pb), % 0
37.3 to 39.3
Manganese (Mn), % 0.4 to 0.8
0
Molybdenum (Mo), % 0.9 to 1.1
0
Nickel (Ni), % 0
0 to 0.010
Nitrogen (N), % 0 to 0.012
0
Phosphorus (P), % 0 to 0.020
0
Silicon (Si), % 0 to 0.5
0
Silver (Ag), % 0
0 to 0.1
Sulfur (S), % 0 to 0.010
0
Tin (Sn), % 0
59.5 to 60.5
Zinc (Zn), % 0
0 to 0.0010