EN 1.7380 Steel vs. SAE-AISI 1117 Steel

Both EN 1.7380 steel and SAE-AISI 1117 steel are iron alloys. They have a very high 96% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.7380 steel and the bottom bar is SAE-AISI 1117 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160 to 170
140 to 150
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 19 to 20
17 to 26
Fatigue Strength, MPa 200 to 230
190 to 300
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 74
73
Shear Strength, MPa 330 to 350
320 to 330
Tensile Strength: Ultimate (UTS), MPa 540 to 550
490 to 540
Tensile Strength: Yield (Proof), MPa 290 to 330
260 to 460

Thermal Properties

Latent Heat of Fusion, J/g 260
250
Maximum Temperature: Mechanical, °C 460
400
Melting Completion (Liquidus), °C 1470
1460
Melting Onset (Solidus), °C 1430
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 39
52
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.6
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 8.7
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 3.8
1.8
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 1.8
1.4
Embodied Energy, MJ/kg 23
18
Embodied Water, L/kg 59
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 87 to 98
86 to 110
Resilience: Unit (Modulus of Resilience), kJ/m3 230 to 280
180 to 550
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 19 to 20
17 to 19
Strength to Weight: Bending, points 19
18 to 19
Thermal Diffusivity, mm2/s 11
14
Thermal Shock Resistance, points 15 to 16
15 to 17

Alloy Composition

Carbon (C), % 0.080 to 0.14
0.14 to 0.2
Chromium (Cr), % 2.0 to 2.5
0
Copper (Cu), % 0 to 0.3
0
Iron (Fe), % 94.6 to 96.6
98.3 to 98.8
Manganese (Mn), % 0.4 to 0.8
1.0 to 1.3
Molybdenum (Mo), % 0.9 to 1.1
0
Nitrogen (N), % 0 to 0.012
0
Phosphorus (P), % 0 to 0.020
0 to 0.040
Silicon (Si), % 0 to 0.5
0
Sulfur (S), % 0 to 0.010
0.080 to 0.13