EN 1.7380 Steel vs. C22000 Bronze
EN 1.7380 steel belongs to the iron alloys classification, while C22000 bronze belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is EN 1.7380 steel and the bottom bar is C22000 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 110 |
| Elongation at Break, % | 19 to 20 | |
| 1.9 to 45 |
| Poisson's Ratio | 0.29 | |
| 0.33 |
| Shear Modulus, GPa | 74 | |
| 42 |
| Shear Strength, MPa | 330 to 350 | |
| 200 to 300 |
| Tensile Strength: Ultimate (UTS), MPa | 540 to 550 | |
| 260 to 520 |
| Tensile Strength: Yield (Proof), MPa | 290 to 330 | |
| 69 to 500 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 200 |
| Maximum Temperature: Mechanical, °C | 460 | |
| 180 |
| Melting Completion (Liquidus), °C | 1470 | |
| 1040 |
| Melting Onset (Solidus), °C | 1430 | |
| 1020 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 390 |
| Thermal Conductivity, W/m-K | 39 | |
| 190 |
| Thermal Expansion, µm/m-K | 13 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.6 | |
| 44 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.7 | |
| 45 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 3.8 | |
| 29 |
| Density, g/cm3 | 7.9 | |
| 8.7 |
| Embodied Carbon, kg CO2/kg material | 1.8 | |
| 2.6 |
| Embodied Energy, MJ/kg | 23 | |
| 42 |
| Embodied Water, L/kg | 59 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 87 to 98 | |
| 3.7 to 230 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 230 to 280 | |
| 21 to 1110 |
| Stiffness to Weight: Axial, points | 13 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 24 | |
| 18 |
| Strength to Weight: Axial, points | 19 to 20 | |
| 8.1 to 17 |
| Strength to Weight: Bending, points | 19 | |
| 10 to 17 |
| Thermal Diffusivity, mm2/s | 11 | |
| 56 |
| Thermal Shock Resistance, points | 15 to 16 | |
| 8.8 to 18 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Carbon (C), % | 0.080 to 0.14 | |
| 0 |
| Chromium (Cr), % | 2.0 to 2.5 | |
| 0 |
| Copper (Cu), % | 0 to 0.3 | |
| 89 to 91 |
| Iron (Fe), % | 94.6 to 96.6 | |
| 0 to 0.050 |
| Lead (Pb), % | 0 | |
| 0 to 0.050 |
| Manganese (Mn), % | 0.4 to 0.8 | |
| 0 |
| Molybdenum (Mo), % | 0.9 to 1.1 | |
| 0 |
| Nitrogen (N), % | 0 to 0.012 | |
| 0 |
| Phosphorus (P), % | 0 to 0.020 | |
| 0 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 8.7 to 11 |
| Residuals, % | 0 | |
| 0 to 0.2 |