EN 1.7380 Steel vs. R30008 Cobalt

EN 1.7380 steel belongs to the iron alloys classification, while R30008 cobalt belongs to the cobalt alloys. There are 23 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is EN 1.7380 steel and the bottom bar is R30008 cobalt.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
210
Elongation at Break, % 19 to 20
1.1 to 73
Fatigue Strength, MPa 200 to 230
320 to 530
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 74
83
Tensile Strength: Ultimate (UTS), MPa 540 to 550
950 to 1700
Tensile Strength: Yield (Proof), MPa 290 to 330
500 to 1080

Thermal Properties

Latent Heat of Fusion, J/g 260
320
Melting Completion (Liquidus), °C 1470
1400
Melting Onset (Solidus), °C 1430
1330
Specific Heat Capacity, J/kg-K 470
450
Thermal Expansion, µm/m-K 13
13

Otherwise Unclassified Properties

Base Metal Price, % relative 3.8
95
Density, g/cm3 7.9
8.4
Embodied Carbon, kg CO2/kg material 1.8
8.1
Embodied Energy, MJ/kg 23
110
Embodied Water, L/kg 59
400

Common Calculations

Resilience: Unit (Modulus of Resilience), kJ/m3 230 to 280
590 to 2720
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 19 to 20
31 to 56
Strength to Weight: Bending, points 19
25 to 37
Thermal Shock Resistance, points 15 to 16
25 to 44

Alloy Composition

Boron (B), % 0
0 to 0.0010
Carbon (C), % 0.080 to 0.14
0 to 0.15
Chromium (Cr), % 2.0 to 2.5
18.5 to 21.5
Cobalt (Co), % 0
39 to 42
Copper (Cu), % 0 to 0.3
0
Iron (Fe), % 94.6 to 96.6
7.6 to 20
Manganese (Mn), % 0.4 to 0.8
1.0 to 2.0
Molybdenum (Mo), % 0.9 to 1.1
6.5 to 7.5
Nickel (Ni), % 0
15 to 18
Nitrogen (N), % 0 to 0.012
0
Phosphorus (P), % 0 to 0.020
0 to 0.015
Silicon (Si), % 0 to 0.5
0 to 1.2
Sulfur (S), % 0 to 0.010
0 to 0.015