EN 1.7701 Steel vs. 2011A Aluminum

EN 1.7701 steel belongs to the iron alloys classification, while 2011A aluminum belongs to the aluminum alloys. There are 24 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN 1.7701 steel and the bottom bar is 2011A aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
70
Poisson's Ratio 0.29
0.33
Shear Modulus, GPa 73
26
Tensile Strength: Ultimate (UTS), MPa 670 to 2010
310 to 410

Thermal Properties

Latent Heat of Fusion, J/g 250
390
Maximum Temperature: Mechanical, °C 420
190
Melting Completion (Liquidus), °C 1460
660
Melting Onset (Solidus), °C 1420
550
Specific Heat Capacity, J/kg-K 470
870
Thermal Conductivity, W/m-K 44
130
Thermal Expansion, µm/m-K 13
23

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
33
Electrical Conductivity: Equal Weight (Specific), % IACS 8.5
96

Otherwise Unclassified Properties

Base Metal Price, % relative 2.6
11
Density, g/cm3 7.8
3.1
Embodied Carbon, kg CO2/kg material 1.9
7.9
Embodied Energy, MJ/kg 26
150
Embodied Water, L/kg 52
1150

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
44
Strength to Weight: Axial, points 24 to 71
28 to 37
Strength to Weight: Bending, points 22 to 45
33 to 40
Thermal Diffusivity, mm2/s 12
49
Thermal Shock Resistance, points 20 to 59
14 to 18

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
91.5 to 95.1
Bismuth (Bi), % 0
0.2 to 0.6
Carbon (C), % 0.48 to 0.56
0
Chromium (Cr), % 0.9 to 1.2
0
Copper (Cu), % 0
4.5 to 6.0
Iron (Fe), % 96.2 to 97.7
0 to 0.5
Lead (Pb), % 0
0.2 to 0.6
Manganese (Mn), % 0.7 to 1.1
0
Molybdenum (Mo), % 0.15 to 0.3
0
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 0 to 0.4
0 to 0.4
Sulfur (S), % 0 to 0.025
0
Vanadium (V), % 0.1 to 0.2
0
Zinc (Zn), % 0
0 to 0.3
Residuals, % 0
0 to 0.15