EN 1.7701 Steel vs. ASTM A182 Grade F11 Class 1

Both EN 1.7701 steel and ASTM A182 grade F11 class 1 are iron alloys. They have a very high 99% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is EN 1.7701 steel and the bottom bar is ASTM A182 grade F11 class 1.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200 to 480
150
Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Tensile Strength: Ultimate (UTS), MPa 670 to 2010
470

Thermal Properties

Latent Heat of Fusion, J/g 250
260
Maximum Temperature: Mechanical, °C 420
430
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 44
39
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 8.5
8.5

Otherwise Unclassified Properties

Base Metal Price, % relative 2.6
2.9
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.9
1.6
Embodied Energy, MJ/kg 26
21
Embodied Water, L/kg 52
52

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 24 to 71
17
Strength to Weight: Bending, points 22 to 45
17
Thermal Diffusivity, mm2/s 12
11
Thermal Shock Resistance, points 20 to 59
14

Alloy Composition

Carbon (C), % 0.48 to 0.56
0.050 to 0.15
Chromium (Cr), % 0.9 to 1.2
1.0 to 1.5
Iron (Fe), % 96.2 to 97.7
96 to 97.7
Manganese (Mn), % 0.7 to 1.1
0.3 to 0.6
Molybdenum (Mo), % 0.15 to 0.3
0.44 to 0.65
Phosphorus (P), % 0 to 0.025
0 to 0.030
Silicon (Si), % 0 to 0.4
0.5 to 1.0
Sulfur (S), % 0 to 0.025
0 to 0.030
Vanadium (V), % 0.1 to 0.2
0