EN 1.7701 Steel vs. AWS BCo-1

EN 1.7701 steel belongs to the iron alloys classification, while AWS BCo-1 belongs to the cobalt alloys. There are 18 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is EN 1.7701 steel and the bottom bar is AWS BCo-1.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Poisson's Ratio 0.29
0.3
Shear Modulus, GPa 73
78
Tensile Strength: Ultimate (UTS), MPa 670 to 2010
700

Thermal Properties

Latent Heat of Fusion, J/g 250
420
Melting Completion (Liquidus), °C 1460
1150
Melting Onset (Solidus), °C 1420
1120
Specific Heat Capacity, J/kg-K 470
480
Thermal Expansion, µm/m-K 13
12

Otherwise Unclassified Properties

Density, g/cm3 7.8
8.1
Embodied Carbon, kg CO2/kg material 1.9
8.0
Embodied Energy, MJ/kg 26
110
Embodied Water, L/kg 52
430

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 24 to 71
24
Strength to Weight: Bending, points 22 to 45
22
Thermal Shock Resistance, points 20 to 59
21

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
0 to 0.050
Boron (B), % 0
0.7 to 0.9
Carbon (C), % 0.48 to 0.56
0.35 to 0.45
Chromium (Cr), % 0.9 to 1.2
18 to 20
Cobalt (Co), % 0
46 to 54
Iron (Fe), % 96.2 to 97.7
0 to 1.0
Manganese (Mn), % 0.7 to 1.1
0
Molybdenum (Mo), % 0.15 to 0.3
0
Nickel (Ni), % 0
16 to 18
Phosphorus (P), % 0 to 0.025
0 to 0.020
Selenium (Se), % 0
0 to 0.0050
Silicon (Si), % 0 to 0.4
7.5 to 8.5
Sulfur (S), % 0 to 0.025
0 to 0.020
Titanium (Ti), % 0
0 to 0.050
Tungsten (W), % 0
3.5 to 4.5
Vanadium (V), % 0.1 to 0.2
0
Zirconium (Zr), % 0
0 to 0.050
Residuals, % 0
0 to 0.5