EN 1.7701 Steel vs. AWS E240

Both EN 1.7701 steel and AWS E240 are iron alloys. They have 66% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is EN 1.7701 steel and the bottom bar is AWS E240.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
77
Tensile Strength: Ultimate (UTS), MPa 670 to 2010
770

Thermal Properties

Latent Heat of Fusion, J/g 250
290
Melting Completion (Liquidus), °C 1460
1390
Melting Onset (Solidus), °C 1420
1350
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 44
15
Thermal Expansion, µm/m-K 13
15

Otherwise Unclassified Properties

Base Metal Price, % relative 2.6
14
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 1.9
3.0
Embodied Energy, MJ/kg 26
42
Embodied Water, L/kg 52
160

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 24 to 71
28
Strength to Weight: Bending, points 22 to 45
24
Thermal Diffusivity, mm2/s 12
3.9
Thermal Shock Resistance, points 20 to 59
19

Alloy Composition

Carbon (C), % 0.48 to 0.56
0 to 0.060
Chromium (Cr), % 0.9 to 1.2
17 to 19
Copper (Cu), % 0
0 to 0.75
Iron (Fe), % 96.2 to 97.7
58.6 to 68.4
Manganese (Mn), % 0.7 to 1.1
10.5 to 13.5
Molybdenum (Mo), % 0.15 to 0.3
0 to 0.75
Nickel (Ni), % 0
4.0 to 6.0
Nitrogen (N), % 0
0.1 to 0.3
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 0 to 0.4
0 to 1.0
Sulfur (S), % 0 to 0.025
0 to 0.030
Vanadium (V), % 0.1 to 0.2
0