EN 1.7701 Steel vs. EN 1.3532 Steel

Both EN 1.7701 steel and EN 1.3532 steel are iron alloys. They have a very high 96% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.7701 steel and the bottom bar is EN 1.3532 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200 to 480
210 to 220
Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Tensile Strength: Ultimate (UTS), MPa 670 to 2010
700 to 1420

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 420
440
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 44
46
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
7.9
Electrical Conductivity: Equal Weight (Specific), % IACS 8.5
9.1

Otherwise Unclassified Properties

Base Metal Price, % relative 2.6
5.0
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.9
1.9
Embodied Energy, MJ/kg 26
25
Embodied Water, L/kg 52
60

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 24 to 71
25 to 50
Strength to Weight: Bending, points 22 to 45
22 to 36
Thermal Diffusivity, mm2/s 12
13
Thermal Shock Resistance, points 20 to 59
21 to 42

Alloy Composition

Aluminum (Al), % 0
0 to 0.050
Carbon (C), % 0.48 to 0.56
0.14 to 0.18
Chromium (Cr), % 0.9 to 1.2
1.0 to 1.4
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 96.2 to 97.7
92.6 to 94.8
Manganese (Mn), % 0.7 to 1.1
0.25 to 0.55
Molybdenum (Mo), % 0.15 to 0.3
0.2 to 0.3
Nickel (Ni), % 0
3.8 to 4.3
Oxygen (O), % 0
0 to 0.0020
Phosphorus (P), % 0 to 0.025
0 to 0.025
Silicon (Si), % 0 to 0.4
0 to 0.4
Sulfur (S), % 0 to 0.025
0 to 0.030
Vanadium (V), % 0.1 to 0.2
0

Comparable Variants