EN 1.7701 Steel vs. C11100 Copper

EN 1.7701 steel belongs to the iron alloys classification, while C11100 copper belongs to the copper alloys. There are 24 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is EN 1.7701 steel and the bottom bar is C11100 copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
120
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 73
44
Tensile Strength: Ultimate (UTS), MPa 670 to 2010
460

Thermal Properties

Latent Heat of Fusion, J/g 250
210
Maximum Temperature: Mechanical, °C 420
200
Melting Completion (Liquidus), °C 1460
1080
Melting Onset (Solidus), °C 1420
1070
Specific Heat Capacity, J/kg-K 470
390
Thermal Conductivity, W/m-K 44
390
Thermal Expansion, µm/m-K 13
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
100
Electrical Conductivity: Equal Weight (Specific), % IACS 8.5
100

Otherwise Unclassified Properties

Base Metal Price, % relative 2.6
31
Density, g/cm3 7.8
9.0
Embodied Carbon, kg CO2/kg material 1.9
2.6
Embodied Energy, MJ/kg 26
41
Embodied Water, L/kg 52
310

Common Calculations

Stiffness to Weight: Axial, points 13
7.2
Stiffness to Weight: Bending, points 24
18
Strength to Weight: Axial, points 24 to 71
14
Strength to Weight: Bending, points 22 to 45
15
Thermal Diffusivity, mm2/s 12
110
Thermal Shock Resistance, points 20 to 59
16

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Carbon (C), % 0.48 to 0.56
0
Chromium (Cr), % 0.9 to 1.2
0
Copper (Cu), % 0
99.9 to 100
Iron (Fe), % 96.2 to 97.7
0
Manganese (Mn), % 0.7 to 1.1
0
Molybdenum (Mo), % 0.15 to 0.3
0
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 0 to 0.4
0
Sulfur (S), % 0 to 0.025
0
Vanadium (V), % 0.1 to 0.2
0
Residuals, % 0
0 to 0.1