EN 1.7701 Steel vs. C36500 Muntz Metal

EN 1.7701 steel belongs to the iron alloys classification, while C36500 Muntz Metal belongs to the copper alloys. There are 24 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is EN 1.7701 steel and the bottom bar is C36500 Muntz Metal.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
100
Poisson's Ratio 0.29
0.3
Shear Modulus, GPa 73
39
Tensile Strength: Ultimate (UTS), MPa 670 to 2010
400

Thermal Properties

Latent Heat of Fusion, J/g 250
170
Maximum Temperature: Mechanical, °C 420
120
Melting Completion (Liquidus), °C 1460
900
Melting Onset (Solidus), °C 1420
890
Specific Heat Capacity, J/kg-K 470
390
Thermal Conductivity, W/m-K 44
120
Thermal Expansion, µm/m-K 13
21

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
28
Electrical Conductivity: Equal Weight (Specific), % IACS 8.5
32

Otherwise Unclassified Properties

Base Metal Price, % relative 2.6
23
Density, g/cm3 7.8
8.0
Embodied Carbon, kg CO2/kg material 1.9
2.7
Embodied Energy, MJ/kg 26
46
Embodied Water, L/kg 52
320

Common Calculations

Stiffness to Weight: Axial, points 13
7.2
Stiffness to Weight: Bending, points 24
20
Strength to Weight: Axial, points 24 to 71
14
Strength to Weight: Bending, points 22 to 45
15
Thermal Diffusivity, mm2/s 12
40
Thermal Shock Resistance, points 20 to 59
13

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Carbon (C), % 0.48 to 0.56
0
Chromium (Cr), % 0.9 to 1.2
0
Copper (Cu), % 0
58 to 61
Iron (Fe), % 96.2 to 97.7
0 to 0.15
Lead (Pb), % 0
0.25 to 0.7
Manganese (Mn), % 0.7 to 1.1
0
Molybdenum (Mo), % 0.15 to 0.3
0
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 0 to 0.4
0
Sulfur (S), % 0 to 0.025
0
Tin (Sn), % 0
0 to 0.25
Vanadium (V), % 0.1 to 0.2
0
Zinc (Zn), % 0
37.5 to 41.8
Residuals, % 0
0 to 0.4