EN 1.7701 Steel vs. C43000 Brass

EN 1.7701 steel belongs to the iron alloys classification, while C43000 brass belongs to the copper alloys. There are 24 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is EN 1.7701 steel and the bottom bar is C43000 brass.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
110
Poisson's Ratio 0.29
0.33
Shear Modulus, GPa 73
42
Tensile Strength: Ultimate (UTS), MPa 670 to 2010
320 to 710

Thermal Properties

Latent Heat of Fusion, J/g 250
190
Maximum Temperature: Mechanical, °C 420
170
Melting Completion (Liquidus), °C 1460
1030
Melting Onset (Solidus), °C 1420
1000
Specific Heat Capacity, J/kg-K 470
380
Thermal Conductivity, W/m-K 44
120
Thermal Expansion, µm/m-K 13
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
27
Electrical Conductivity: Equal Weight (Specific), % IACS 8.5
28

Otherwise Unclassified Properties

Base Metal Price, % relative 2.6
29
Density, g/cm3 7.8
8.6
Embodied Carbon, kg CO2/kg material 1.9
2.8
Embodied Energy, MJ/kg 26
46
Embodied Water, L/kg 52
330

Common Calculations

Stiffness to Weight: Axial, points 13
7.1
Stiffness to Weight: Bending, points 24
19
Strength to Weight: Axial, points 24 to 71
10 to 23
Strength to Weight: Bending, points 22 to 45
12 to 20
Thermal Diffusivity, mm2/s 12
36
Thermal Shock Resistance, points 20 to 59
11 to 25

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Carbon (C), % 0.48 to 0.56
0
Chromium (Cr), % 0.9 to 1.2
0
Copper (Cu), % 0
84 to 87
Iron (Fe), % 96.2 to 97.7
0 to 0.050
Lead (Pb), % 0
0 to 0.1
Manganese (Mn), % 0.7 to 1.1
0
Molybdenum (Mo), % 0.15 to 0.3
0
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 0 to 0.4
0
Sulfur (S), % 0 to 0.025
0
Tin (Sn), % 0
1.7 to 2.7
Vanadium (V), % 0.1 to 0.2
0
Zinc (Zn), % 0
9.7 to 14.3
Residuals, % 0
0 to 0.5