MakeItFrom.com
Menu (ESC)

EN 1.7701 Steel vs. C75400 Nickel Silver

EN 1.7701 steel belongs to the iron alloys classification, while C75400 nickel silver belongs to the copper alloys. There are 24 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is EN 1.7701 steel and the bottom bar is C75400 nickel silver.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
120
Poisson's Ratio 0.29
0.32
Shear Modulus, GPa 73
46
Tensile Strength: Ultimate (UTS), MPa 670 to 2010
370 to 630

Thermal Properties

Latent Heat of Fusion, J/g 250
200
Maximum Temperature: Mechanical, °C 420
190
Melting Completion (Liquidus), °C 1460
1080
Melting Onset (Solidus), °C 1420
1040
Specific Heat Capacity, J/kg-K 470
390
Thermal Conductivity, W/m-K 44
36
Thermal Expansion, µm/m-K 13
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 8.5
7.4

Otherwise Unclassified Properties

Base Metal Price, % relative 2.6
32
Density, g/cm3 7.8
8.5
Embodied Carbon, kg CO2/kg material 1.9
3.8
Embodied Energy, MJ/kg 26
59
Embodied Water, L/kg 52
300

Common Calculations

Stiffness to Weight: Axial, points 13
7.9
Stiffness to Weight: Bending, points 24
19
Strength to Weight: Axial, points 24 to 71
12 to 21
Strength to Weight: Bending, points 22 to 45
13 to 19
Thermal Diffusivity, mm2/s 12
11
Thermal Shock Resistance, points 20 to 59
12 to 21

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Carbon (C), % 0.48 to 0.56
0
Chromium (Cr), % 0.9 to 1.2
0
Copper (Cu), % 0
63.5 to 66.5
Iron (Fe), % 96.2 to 97.7
0 to 0.25
Lead (Pb), % 0
0 to 0.1
Manganese (Mn), % 0.7 to 1.1
0 to 0.5
Molybdenum (Mo), % 0.15 to 0.3
0
Nickel (Ni), % 0
14 to 16
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 0 to 0.4
0
Sulfur (S), % 0 to 0.025
0
Vanadium (V), % 0.1 to 0.2
0
Zinc (Zn), % 0
16.2 to 22.5
Residuals, % 0
0 to 0.5