EN 1.7701 Steel vs. C83300 Brass

EN 1.7701 steel belongs to the iron alloys classification, while C83300 brass belongs to the copper alloys. There are 25 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.7701 steel and the bottom bar is C83300 brass.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200 to 480
35
Elastic (Young's, Tensile) Modulus, GPa 190
110
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 73
42
Tensile Strength: Ultimate (UTS), MPa 670 to 2010
220

Thermal Properties

Latent Heat of Fusion, J/g 250
200
Maximum Temperature: Mechanical, °C 420
180
Melting Completion (Liquidus), °C 1460
1060
Melting Onset (Solidus), °C 1420
1030
Specific Heat Capacity, J/kg-K 470
380
Thermal Conductivity, W/m-K 44
160
Thermal Expansion, µm/m-K 13
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
32
Electrical Conductivity: Equal Weight (Specific), % IACS 8.5
33

Otherwise Unclassified Properties

Base Metal Price, % relative 2.6
30
Density, g/cm3 7.8
8.8
Embodied Carbon, kg CO2/kg material 1.9
2.7
Embodied Energy, MJ/kg 26
44
Embodied Water, L/kg 52
320

Common Calculations

Stiffness to Weight: Axial, points 13
7.0
Stiffness to Weight: Bending, points 24
18
Strength to Weight: Axial, points 24 to 71
6.9
Strength to Weight: Bending, points 22 to 45
9.2
Thermal Diffusivity, mm2/s 12
48
Thermal Shock Resistance, points 20 to 59
7.9

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Carbon (C), % 0.48 to 0.56
0
Chromium (Cr), % 0.9 to 1.2
0
Copper (Cu), % 0
92 to 94
Iron (Fe), % 96.2 to 97.7
0
Lead (Pb), % 0
1.0 to 2.0
Manganese (Mn), % 0.7 to 1.1
0
Molybdenum (Mo), % 0.15 to 0.3
0
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 0 to 0.4
0
Sulfur (S), % 0 to 0.025
0
Tin (Sn), % 0
1.0 to 2.0
Vanadium (V), % 0.1 to 0.2
0
Zinc (Zn), % 0
2.0 to 6.0
Residuals, % 0
0 to 0.7