EN 1.7701 Steel vs. C86100 Bronze

EN 1.7701 steel belongs to the iron alloys classification, while C86100 bronze belongs to the copper alloys. There are 24 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.7701 steel and the bottom bar is C86100 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
110
Poisson's Ratio 0.29
0.32
Shear Modulus, GPa 73
43
Tensile Strength: Ultimate (UTS), MPa 670 to 2010
660

Thermal Properties

Latent Heat of Fusion, J/g 250
200
Maximum Temperature: Mechanical, °C 420
170
Melting Completion (Liquidus), °C 1460
940
Melting Onset (Solidus), °C 1420
900
Specific Heat Capacity, J/kg-K 470
420
Thermal Conductivity, W/m-K 44
35
Thermal Expansion, µm/m-K 13
20

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
8.0
Electrical Conductivity: Equal Weight (Specific), % IACS 8.5
9.0

Otherwise Unclassified Properties

Base Metal Price, % relative 2.6
24
Density, g/cm3 7.8
8.0
Embodied Carbon, kg CO2/kg material 1.9
2.9
Embodied Energy, MJ/kg 26
49
Embodied Water, L/kg 52
350

Common Calculations

Stiffness to Weight: Axial, points 13
7.8
Stiffness to Weight: Bending, points 24
20
Strength to Weight: Axial, points 24 to 71
23
Strength to Weight: Bending, points 22 to 45
21
Thermal Diffusivity, mm2/s 12
10
Thermal Shock Resistance, points 20 to 59
21

Alloy Composition

Aluminum (Al), % 0
4.5 to 5.5
Carbon (C), % 0.48 to 0.56
0
Chromium (Cr), % 0.9 to 1.2
0
Copper (Cu), % 0
66 to 68
Iron (Fe), % 96.2 to 97.7
2.0 to 4.0
Lead (Pb), % 0
0 to 0.1
Manganese (Mn), % 0.7 to 1.1
2.5 to 5.0
Molybdenum (Mo), % 0.15 to 0.3
0
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 0 to 0.4
0
Sulfur (S), % 0 to 0.025
0
Tin (Sn), % 0
0 to 0.1
Vanadium (V), % 0.1 to 0.2
0
Zinc (Zn), % 0
17.3 to 25