EN 1.7709 Steel vs. SAE-AISI 1548 Steel

Both EN 1.7709 steel and SAE-AISI 1548 steel are iron alloys. They have a very high 97% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is EN 1.7709 steel and the bottom bar is SAE-AISI 1548 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200 to 230
220 to 250
Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
72
Tensile Strength: Ultimate (UTS), MPa 650 to 780
730 to 830

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 440
400
Melting Completion (Liquidus), °C 1470
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 33
51
Thermal Expansion, µm/m-K 11
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.5
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 8.6
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 3.4
1.8
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 2.3
1.4
Embodied Energy, MJ/kg 32
19
Embodied Water, L/kg 56
47

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 23 to 27
26 to 30
Strength to Weight: Bending, points 21 to 24
23 to 25
Thermal Diffusivity, mm2/s 8.9
14
Thermal Shock Resistance, points 22 to 26
23 to 27

Alloy Composition

Aluminum (Al), % 0 to 0.030
0
Carbon (C), % 0.17 to 0.25
0.44 to 0.52
Chromium (Cr), % 1.2 to 1.5
0
Iron (Fe), % 95.2 to 97.5
98 to 98.5
Manganese (Mn), % 0.4 to 0.8
1.1 to 1.4
Molybdenum (Mo), % 0.55 to 0.8
0
Nickel (Ni), % 0 to 0.6
0
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 0 to 0.4
0
Sulfur (S), % 0 to 0.030
0 to 0.050
Vanadium (V), % 0.2 to 0.35
0