EN 1.7711 Steel vs. AISI 310 Stainless Steel

Both EN 1.7711 steel and AISI 310 stainless steel are iron alloys. They have 55% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.7711 steel and the bottom bar is AISI 310 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210 to 280
180 to 220
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 16 to 22
34 to 45
Fatigue Strength, MPa 290 to 520
240 to 280
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 73
78
Shear Strength, MPa 440 to 570
420 to 470
Tensile Strength: Ultimate (UTS), MPa 690 to 930
600 to 710
Tensile Strength: Yield (Proof), MPa 400 to 800
260 to 350

Thermal Properties

Latent Heat of Fusion, J/g 250
310
Maximum Temperature: Mechanical, °C 430
1040
Melting Completion (Liquidus), °C 1460
1450
Melting Onset (Solidus), °C 1420
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 33
15
Thermal Expansion, µm/m-K 11
15

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.5
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 3.0
25
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 2.3
4.3
Embodied Energy, MJ/kg 32
61
Embodied Water, L/kg 54
190

Common Calculations

PREN (Pitting Resistance) 2.9
25
Resilience: Ultimate (Unit Rupture Work), MJ/m3 130 to 140
200 to 220
Resilience: Unit (Modulus of Resilience), kJ/m3 430 to 1690
170 to 310
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 24 to 33
21 to 25
Strength to Weight: Bending, points 22 to 27
20 to 22
Thermal Diffusivity, mm2/s 8.9
3.9
Thermal Shock Resistance, points 24 to 32
14 to 17

Alloy Composition

Aluminum (Al), % 0 to 0.015
0
Carbon (C), % 0.36 to 0.44
0 to 0.25
Chromium (Cr), % 0.9 to 1.2
24 to 26
Iron (Fe), % 96 to 97.5
48.2 to 57
Manganese (Mn), % 0.45 to 0.85
0 to 2.0
Molybdenum (Mo), % 0.5 to 0.65
0
Nickel (Ni), % 0
19 to 22
Phosphorus (P), % 0 to 0.025
0 to 0.045
Silicon (Si), % 0 to 0.4
0 to 1.5
Sulfur (S), % 0 to 0.030
0 to 0.030
Vanadium (V), % 0.25 to 0.35
0